The integration of additive manufacturing (3D printing) in the biomedical sector required material to portray a holistic characteristic in terms of printability, biocompatibility, degradability, and mechanical properties. This research aims to evaluate the 3D printability and mechanical properties of polyhydroxybutyrate (PHB) as additives in the urethane dimethacrylate (UDMA) based resin and its potential for medical applications. The printability of the PHB/UDMA resin blends was limited to 11 wt.% as it reached the maximum viscosity value at 2188 cP. Two-way analysis of variance (ANOVA) was also conducted to assess the significant effect of the varied PHB (wt.%) incorporation within UDMA resin, and the aging duration of 3D printed PHB/UDMA on mechanical properties in terms of tensile and impact properties. Meanwhile, the increasing crystallinity index (CI) of X-ray diffraction (XRD) in the 3D printed PHB/UDMA as the PHB loading increased, indicating that there is a strong correlation with the lower tensile and impact strength. FESEM images also proved that the agglomerations that occurred within the UDMA matrix had affected the mechanical performance of 3D printed PHB/UDMA. Nonetheless, the thermal stability of the 3D printed PHB/UDMA had only a slight deviation from the 3D printed UDMA since it had better thermal processability.

In this work, a plant-based resin gel polymer electrolyte (GPE) was prepared by stereolithography (SLA) 3D printing. Lithium perchlorate (LiClO4) with a concentration between 0 wt.% and 25 wt.% was added into the plant-based resin to observe its influence on electrical and structural characteristics. Fourier transform infrared spectroscopy (FTIR) analysis showed shifts in the carbonyl, ester, and amine groups, proving that complexation between the polymer and LiClO4 had occurred. GPEs with a 20 wt.% LiClO4 (S20) showed the highest room temperature conductivity of 3.05 × 10−3 S cm−1 due to the highest number of free ions as determined from FTIR deconvolution. The mobility of free ions in S20 electrolytes was also the highest due to greater micropore formation, as observed via field emission scanning electron microscopy (FESEM) images. Transference number measurements suggest that ionic mobility plays a pivotal role in influencing the conductivity of S20 electrolytes. Based on this work, it can be concluded that the plant-based resin GPE with LiClO4 is suitable for future electrochemical applications.

Today, additive manufacturing (AM) is considered one of the vital tenets of the industry 4.0 revolution due to its high productivity, decentralized production and rapid prototyping. This work aims to study the mechanical and structural properties of polyhydroxybutyrate as an additive in blend materials and its potential in medical applications. PHB/PUA blend resins were formulated with 0 wt.%, 6 wt.%, 12 wt.% and 18 wt.% of PHB concentration. Stereolithography or an SLA 3D printing technique were used to evaluate the printability of the PHB/PUA blend resins. Additionally, from FESEM analysis, a change was observed in PUA’s microstructure, with an additional number of voids spotted. Furthermore, from XRD analysis, as PHB concentration increased, the crystallinity index (CI) also increased. This indicates the brittleness properties of the materials, which correlated to the weak performance of the tensile and impact properties. Next, the effect of PHB loading concentration within PHB/PUA blends and aging duration towards the mechanical performance of tensile and impact properties was also studied by using analysis of variance (ANOVA) with a two-way method. Finally, 12 wt.% of PHB/PUA was selected to 3D print the finger splint due to its characteristics, which are compatible to be used in finger bone fracture recovery.