Graphene based macrobend unclad smf for monitoring ph level in aqueous environment

Partial unclad fibers with diameters ranging from d=121µm to d=125µm were fabricated using standard telecommunications optical fiber (SMF28) via low cost mechanical swipe-off technique. Graphene oxide (GO) was deposited using drop casting method on the outer side of the partial unclad SMF. IR laser with excitation wavelengths of λ=1310nm and λ=1550nm were launched along the graphene-coated SMF. The sensitivity of graphene based macrobend unclad SMFs were investigated by introducing two different pH of aqueous environment with values of 3.5 (acidic) and 12.5 (alkaline) that acted as sensing media. The optimum power loss was obtained as smallest diameter of partial unclad SMF with d=121µm was appointed. As uncoated SMF was replaced with the GO coated SMF which had been immersed into 3.5pH liquid solution, it was found that the optical power losses were increased about 6.79dBm and 5.15dBm using laser with λ1=1310nm and λ2=1550nm respectively. The uncoated SMFs experienced the increment of power losses about 2.11dBm and 5.15dBm as they were soaked into the solution with pH=12.5 using similar laser of λ1 and λ2. It is noteworthy to highlight the significant of graphene’s employment on macrobend unclad SMF by using λ1=1310nm in which better sensitivity and selectivity represented by maximum changes of power losses were apparently observed for both solutions. The usage of λ=1550nm exhibited poor selectivity where the partial unclad SMF unable to differentiate two contrasting pH solution. In conclusion, graphene based macrobend fiber optic sensor for pH detection was successfully developed by employing partial unclad SMF with cladding diameter of d=121µm and laser wavelength of λ=1310nm due to the enhancement of evanescent field’s strength. © 2020 Trans Tech Publications Ltd, Switzerland.