Diabetes is a metabolic disease with a prolonged elevated level of glucose in the blood leads to long-term complications and increases the chances for cardiovascular diseases. The present study describes the fabrication of a ZnO nanowire (NW)-modified interdigitated electrode (IDE) to monitor the level of blood glucose. A silver IDE was generated by wet etching-assisted conventional lithography, with a gap between adjacent electrodes of 98.80 μm. The ZnO-based thin films and NWs were amended by sol–gel and hydrothermal routes. High-quality crystalline and c-axis orientated ZnO thin films were observed by XRD analyses. The ZnO thin film was annealed for 1, 3 and 5 h, yielding a good-quality crystallite with sizes of 50, 100 and 110 nm, and the band gaps were measured as 3.26, 3.20 and 3.17 eV, respectively. Furthermore, a flower-modeled NW was obtained with the lowest diameter of 21 nm. Our designed ZnO NW-modified IDE was shown to have a detection limit as low as 0.03 mg/dL (correlation coefficient = 0.98952) of glucose with a low response time of 3 s, perform better than commercial glucose meter, suitable to instantly monitor the glucose level of diabetes patients. This study demonstrated the high performance of NW-mediated IDEs for glucose sensing as alternative to current glucose sensors

Creating novel nanostructures is a primary step for high-performance analytical sensing. Herein, a new worm like nanostructure with Zinc Oxide-gold (ZnO/Au) hybrid was fabricated through an aqueous hydrothermal method, by doping Au-nanoparticle (AuNP) on the growing ZnO lattice. During ZnO growth, fine tuning the solution temperature expedites random curving of ZnO nanorods and forms nano-worms. The nano-worms which were evidenced by morphological, physical and structural analyses, revealed elongated structures protruding from the surface (length: 1 µm; diameter: ~100 nm). The appropriate peaks for the face centred cubic gold were (111) and (200), as seen from X-ray diffractogram. The strong interrelation between Au and ZnO was manifested by X-ray photoelectron spectroscopy. The combined surface area increment from the nanoparticle radii and ZnO nanorod random curving gives raise an enhancement in detection sensitivity by increasing bio-loading. ‘Au-decorated hybrid nano-worm’ was immobilized with a probe DNA from Vibrio Cholera and duplexed with a target which was revealed by Fourier Transform Infrared Spectroscopy. Our novel Au-decorated hybrid nano-worm is suitable for high-performance bio-sensing, as evidenced by impedance spectroscopy, having higher-specificity and attained femtomolar (10 fM) sensitivity. Further, higher stability, reproducibility and regeneration on this sensing surface were demonstrated.